Stainless Steel
| Alloy components | |||
|---|---|---|---|
| C |
max. 0,07 |
Si |
1,50 |
| Mn |
1,50 |
P |
0,040 |
| S |
0,030 |
Cr |
18,00 bis 20,00 |
| Mo |
– |
Ni |
8,00 bis 11,00 |
| N |
– |
Cu |
– |
| Nb |
– |
W |
– |
| Material properties (+AT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
175 |
||
| Tensile strength Rm MPa min. |
440 |
||
| Elongation at break A % min. |
30 |
||
| notched flexural impact test KV2 J min. |
60 |
||
| Alloy components | |||
|---|---|---|---|
| C |
max. 0,07 |
Si |
1,50 |
| Mn |
1,50 |
P |
0,040 |
| S |
0,030 |
Cr |
18,00 bis 20,00 |
| Mo |
2,00 bis 2,50 |
Ni |
9,00 bis 12,00 |
| N |
– |
Cu |
– |
| Nb |
– |
W |
– |
| Material properties (+AT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
185 |
||
| Tensile strength Rm MPa min. |
440 |
||
| Elongation at break A % min. |
30 |
||
| notched flexural impact test KV2 J min. |
60 |
||
| Alloy components | |||
|---|---|---|---|
| C |
max. 0,07 |
Si |
1,50 |
| Mn |
1,50 |
P |
0,040 |
| S |
0,030 |
Cr |
18,00 bis 20,00 |
| Mo |
2,00 bis 2,50 |
Ni |
9,00 bis 12,00 |
| N |
– |
Cu |
– |
| Nb |
– |
W |
8 x% C < 1,00 |
| Material properties (+AT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
185 |
||
| Tensile strength Rm MPa min. |
440 |
||
| Elongation at break A % min. |
25 |
||
| notched flexural impact test KV2 J min. |
40 |
||
| Alloy components | |||
|---|---|---|---|
| C |
0,16 bis 0,23 |
Si |
1,00 |
| Mn |
1,00 |
P |
0,045 |
| S |
0,030 |
Cr |
12,50 bis 14,50 |
| Mo |
– |
Ni |
1,00 |
| N |
– |
Cu |
– |
| Nb |
– |
W |
-< 1,00 |
| Material properties (+QT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
440 |
||
| Tensile strength Rm MPa min. |
590 |
||
| Elongation at break A % min. |
12 |
||
| notched flexural impact test KV2 J min. |
– |
||
| Alloy components | |||
|---|---|---|---|
| C |
max. 0,030 |
Si |
1,00 |
| Mn |
1,50 |
P |
0,035 |
| S |
0,025 |
Cr |
24,50 bis 26,50 |
| Mo |
2,50 bis 3,50 |
Ni |
5,00 bis 7,00 |
| N |
0,12 bis 0,22 |
Cu |
2,75 bis 3,50 |
| Nb |
– |
W |
-< 1,00 |
| Material properties (+AT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
480 |
||
| Tensile strength Rm MPa min. |
650 |
||
| Elongation at break A % min. |
22 |
||
| notched flexural impact test KV2 J min. |
50 |
||
| Alloy components | |||
|---|---|---|---|
| C |
max. 0,025 |
Si |
1,00 |
| Mn |
2,00 |
P |
0,035 |
| S |
0,020 |
Cr |
19,00 bis 21,00 |
| Mo |
6,00 bis 7,00 |
Ni |
24,00 bis 26,00 |
| N |
0,10 bis 0,25 |
Cu |
0,50 bis 1,50 |
| Nb |
– |
W |
-< 1,00 |
| Material properties (+AT) | |||
|---|---|---|---|
| Yield strength Rp0,2 MPa min. |
210 |
||
| Tensile strength Rm MPa min. |
480 |
||
| Elongation at break A % min. |
30 |
||
| notched flexural impact test KV2 J min. |
60 |
||
We will be happy to advise you on the right material for your product and application.